Classification Composition [%] Applications
DIN 8555 E 7-UM-250-KP
AWS A 5.13 E FeMn-A
HB 250		 C : 0.8
Mn : 14
Cr : 3		 Basic coated, AC-weldable electrode. Suitable for hardfacing on parts which are subject to extreme impact stress and cavitation.
DIN 8555 E 1-UM-300-P
AWS A 5.13 E Fe 1
HB 300		 C : 0.1
Si : 0.5
Mn : 1
Cr : 1.2		 AC-weldable electrode for tough and wear resistant surfacing on equipment parts and tools which are subject to medium wear only.
DIN 8555 E 1-UM-350-P
AWS A 5.13 E Fe 1
HB 350		 C : 0.15
Si : 0.5
Mn : 1
Cr : 3		 AC-weldable electrode for tough and wear resistant surfacing on equipment parts and tools which are subject to medium wear only.
DIN 8555 E 10-UM-60-GR
AWS A 5.13 EFeCr-A1
HRC 57		 C : 4.5
Si : 1
Cr : 28
Others : 2		 Heavy coated high efficiency hardfacing electrode depositing a ledeburitic structure. It is used for hardfacing of parts subject to strong abrasive wear, friction also at high temperatures.
DIN 8555 E 10-UM-60-GR
AWS A 5.13 EFeCr-A1
HRC 59		 C : 3.8
Si : 0.9
Cr : 33 Others: 2		 Heavy coated high efficiency hardfacing electrode depositing a ledeburitic structure. It is used for hardfacing of parts subject to strong abrasive wear, friction also at high temperatures.
DIN 8555 E 10-UM-65-GRZ
AWS A 5.13 EFeCr-A1
HRC 64		 C : 4.5
Si : 1.2
Cr : 24
Mo : 6
Nb : 6.2
W : 2
V : 1 		Heavy coated high efficiency hardfacing electrode. Suitable for applications subject to strong abrasive wear by minerals, combined with moderate impact, medium shocks and compression as well as humidity or wetness.
DIN 8555 E 10-UM-70-GTRZ
AWS A 5.13 EFeCr-A1
HRC 69		 C : 5.5
Si : 2
Cr : 35
Others: 4 		Heavy coated high efficiency hardfacing electrode. Suitable for applications where parts are subject to strong abrasive wear since the deposited alloy is highly resistant to abrasion, also when exposed to high temperatures.